| (a) Cotton. (1) The term "cotton" by itself shall not be used. (2) Staple cotton is the fibrous growth as removed from the cottonseed in the usual process of ginning (first-cut from the seed). (3) Cotton linters are the fibrous growth removed from the cottonseed subsequent to the usual process of ginning. The term "linters" alone shall not be used. (4) Cotton by-product is a loose filling material consisting of cotton fibers which have been removed from the various machine operations in the preparation and manufacture of cotton yarn up to, but not including, the process of spinning, and shall include only the following materials commonly known in cotton mill terms as: (A) cotton card or vacuum strips; (B) cotton comber; (C) cotton fly; (D) cotton picker or motes. (5) The term "blended cotton felt" or "blended cotton batting" shall be used when a mixture of cotton fiber is made into felt form. (b) Down. (1) The term "down" by itself may be used for the soft undercoating of waterfowl consisting of the light fluffy filaments grown from one quill-point but without any quill shaft. It is permissable to use the name of the fowl from which the down is obtained, such as goose down, duck down, etc. (2) Plumules are downy waterfowl plumage with underdeveloped soft and flaccid quill with barbs indistinguishable from those of down. (3) Down fiber is the detached barbs from down plumes and plumules separated from the quill point. (4) Nestling down is a down not fully developed with a short sheath with relatively long soft barbs emanating from sheath. (5) The tolerance levels for the labeling of down are as follows: (A) a minimum of 80% down, plumules, and down fiber; (i) consisting of down and plumules--minimum of 70%; (ii) consisting of down fiber--minimum of 10%; (B) the remaining 20% may consist of a combination of the following: (i) natural waterfowl feathers; (ii) down fiber; (iii) damaged feathers--maximum 3.0%; (iv) chicken feather and fiber--maximum 2.0%; (v) residue--maximum 2.0%; (vi) waterfowl feather fiber. (6) Species designation tolerance. If the down product is labeled as to the waterfowl (goose or duck), a minimum of 90% of the waterfowl plumage contained therein must be of that species. (c) Feathers. (1) The term "feathers" by itself shall not be used. (2) Goose feathers are feathers of any kind of goose, which are whole in physical structure, with the natural form and curvature of the feather. (3) Duck feathers are feathers of any kind of duck, which are whole in physical structure, with the natural form and curvature of the feather. (4) Waterfowl feathers may be used to designate any mixture of goose and duck feathers. (5) Turkey feathers are feathers of any kind of turkey, which are whole in physical structure. (6) Chicken feathers are feathers of any kind of chicken, which are whole in physical structure. (7) Emu feathers are feathers of any kind of emu, which are whole in physical structure. (8) Damaged feathers, in conjunction with the name of the fowl from which the feathers come, shall mean feathers which have been broken, injured by insects or depreciated from the original value in any manner and which exceeds the 10% allowable tolerance. (9) Crushed feathers, in conjunction with the name of the fowl from which the feathers come, shall mean feathers which have been processed by a curling, crushing, or chopping machine. (10) Feather mixtures when from two or more species shall be designated by name, character, and percentage by weight of each constituent in order of predominance, or mixtures may be designated by lowest grade as to species of origin (grades in descending order: goose, duck, turkey, chicken). (d) Foam. (1) The term "foam" by itself shall not be used. (2) Foam is polymerized material consisting of a mass of thin-walled cells produced chemically or physically which is created by the interaction of an ester or an ether and carbamic acid derivative. (3) The term "synthetic foam" may be used as a definition in lieu of the following generic terms: (A) polyurethane foam; (B) urethane foam; (C) polyester foam; (D) polyether foam; (E) vinyl foam; and (F) polystyrene foam. (4) Urethane foam high resilience is a permissible term for urethane foam with a minimum density of 2.5 pounds per cubic foot, a minimum resilience of 60%, and a minimum support ratio of 2.4 pounds per cubic foot. (5) Polystyrene foam beads are a filling material which has been processed into small round droplets approximately 1/2 inch in diameter, or less. (6) When generic terms are used for foam products, they shall be true and correct. (e) Hair. (1) Hair--The coarse filamentous epidermal outgrowth of such mammals as horses, cattle, hogs, and goats when used in the manufacture of bedding, upholstered furniture, and filling materials. It shall be clean, properly cured, free from epidermis, excreta, and other foreign or objectionable substances and odors. (2) Hair mixtures--The hair of different animal origin used in a blend or mixture. The kind and percentage, by weight of each, shall be stated on the label. Where materials other than hair are used with hair in a mixture, the kind and percentage by weight of each material shall be stated on the label. (f) Manufactured fibers. (1) Acetate fiber--Manufactured fiber in which the fiber-forming substance is cellulose acetate. Where not less than 92% of hydroxyl groups are acetylated, the term triacetate may be used as generic description of the fiber. (2) Acrylic fiber--Manufactured fiber in which the fiber-forming substance is any long chain synthetic polymer composed of at least 85% by weight of acrylonitrile units. (3) Azlon fiber--Manufactured fiber in which the fiber-forming substance is composed of any regenerated naturally occurring proteins. (4) Glass fiber--Manufactured fiber in which the fiber-forming substance is glass. (5) Metallic fiber--Manufactured fiber composed of metal, plastic-coated metal, metal-coated plastic, or core completely covered by metal. (6) Modacrylic fiber--Manufactured fiber in which the fiber-forming substance is any long chain synthetic polymer composed of less than 85%, but at least 35% by weight, of acrylonitrile units. (7) Nylon fiber--Manufactured fiber in which the fiber-forming substance is any long chain synthetic polyamide having recurring amide groups. (8) Nytril fiber--Manufactured fiber containing at least 85% of long chain polymer of vinylidene dinitrile when the vinylidene dinitrile content is no less than every other unit in the polymer chain. (9) Olefin fiber--Manufactured fiber in which the fiber-forming substance is any long chain synthetic polymer composed of at least 85% by weight of ethylene, propylene, or other olefin units. (10) Polyester fiber--Manufactured fiber in which the fiber-forming substance is any long chain synthetic polymer composed of at least 85% by weight of any ester of a dihydric alcohol and terephthalic acid. (11) Rayon fiber--Manufactured fiber composed of regenerated cellulose, as well as manufactured fibers composed of regenerated cellulose in which substituents have replaced not more than 15% of the hydrogens of the hydroxyl groups. (12) Saran fiber--Manufactured fiber in which the fiber-forming substance is any long chain synthetic polymer composed of at least 80% by weight of vinylidene chloride units. (13) Spandex fiber--Manufactured fiber in which the fiber-forming substance is a long chain synthetic polymer comprised of at least 85% of a segmented polyurethane. (14) Vinyl fiber--Manufactured fiber in which the fiber-forming substance is any long chain synthetic polymer composed of at least 50% by weight of vinyl alcohol units, and in which the total of the vinyl alcohol units and any one or more of the various acetal units is at least 85% by weight of the fiber. (15) Vinyon fiber--Manufactured fiber in which the fiber-forming substance is any long chain synthetic polymer composed of at least 85% by weight of vinyl chloride units. (16) Polyester pneumacel--A generic term for a polyester pneumatic cellular product. Cont'd... |
